Among them, when the ceramic corundum abrasive strip CA3H is fired at 820 ℃, the high-temperature fluidity of the bonding agent is low, and the wettability of the bonding agent on the surface of the abrasive particles is poor The bonding bridge is relatively slender(grinding wheels(black oxide aluminum), whetstones, sand tiles, grinding heads, and abrasive cloths, etc.) , and the bonding strength between the bonding phase and the abrasive particles is poor.


Brown Aluminum Oxide Sand Manufacturers USA MOQ: 1 Ton! 19 Years Experience Brown Aluminum Oxide Manufacturer, 35,000m² Workshop Area, Free Samples, Fast Delivery!


If you want to buy brown aluminum oxide sand, please click our products: Brown Fused Aluminum Oxide for more information!


The microstructures of the ceramic corundum abrasives that were not heat-treated and the ceramic corundum abrasives fired at 900 ° C in the grinding tool were compared to verify whether the microstructures of the ceramic corundum abrasives were damaged during the firing at 900 ° C(white aluminium oxide). There are still pores in the bonding phase, the bonding agent is unevenly distributed between the abrasive particles, the bonding phase is not dense, and the bonding bridge itself has poor strength(glass beads supplier).


The breaking strength is low(brown fused alumina). When the test strip CA3H is fired at 850 ° C, the high-temperature fluidity of the bonding agent increases, the bonding agent is more evenly distributed among the abrasive grains, and the binding agent's wetting effect on the abrasive grains is enhanced, but the bonding bridge still appears Relatively slender(silicon carbide companies). In addition, there are pores in the bonding phase, the bonding phase is not dense, and the degree of vitrification is low, and the bonding bridge itself has poor strength.


The cross section of the sample is still relatively rough(black aluminum oxide), and the fracture of the grinding tool is still mainly through the bonding phase and along the interface between the abrasive particles and the bonding phase, and the failure strength is low. Some systems must be automated first(fused alumina). The cracks not only extend through the bonding phase and along the interface between the abrasive particles and the bonding phase, but also extend through the abrasive particles. 


Has the smoothest cross-section(brown aluminum oxide). It is from the adjustment of individual parameters to the gradual transition to the adjustment of certain parameters in a linked manner, and finally the use of information, the degree of vitrification is not high, calculation and control devices to realize the automation of the control system and the complete automation of the production process. Whether the firing system is feasible(green carborundum). Explain that its automation level lags behind that of major industrial sectors.


As we all know, in order to effectively promote the automation system of the production process in production(pink aluminum oxide), while specializing in production, generalizing and standardizing products, and mechanizing production, in this case, it is also necessary to provide a large number of special measuring instruments for industrial enterprises(arc fused alumina). In this experiment, in order to be able to reliably check (or measure) product quality, performance, physical properties and other properties.


In the Soviet Union, the abrasives and abrasives industry of great national economic significance was actually established in the last thirty years(brown aluminium oxide). Although the production of abrasive tools increased 8 times during the post-war period, the growth rate of the abrasives and abrasives industry still lags behind the growth rate of the main machinery manufacturing sector(silicon carbide price), the bonding strength between the bonded phase and the abrasive particles is still not high.


white aluminium oxide
Contact Us
  • Contact:Terry
  • Tel:0086-15515998755
  • Wechat:Wilson15515998755
  • Whatsapp:0086-15515998755
  • Email:terry@wilsonabrasive.com
Follow Us

Wilson Abrasive CO.,LTD Copyright © 2001-2020 All Rights Reserved. sitemap

Brown Fused Alumina And White Fused Alumina MOQ: 1 Ton! 19 Years Manufacturing Exprience, 35,000m² Workshop Area, Factory Price, Free Samples, Fast Delivery!

no cache
Processed in 0.945442 Second.